Solar Profiling explained at Hamburg Solar Energy Conference

MB (Marybeth) Allen is interviewed by Philip Stoten of PVP Now at the European Photovoltaic Solar Energy Conference and Exhibition in Hamburg, Germany.

MB shows offs some of the features of the e-Clipse a new way to hold solar wafers without destroying them in the profiling process.

Also MB discusses Spectrum, KIC’s optimization software that is yielding real savings in the Photovoltaic manufacturing industry.  A recent published study was discussed in my last blog.

MB interview

Click here to see the full interview.


Increasing Silicon Solar Efficiency Manufacturing

Global Solar Technology printed an article on Sept 16, 2009 highlighting an exciting ground breaking study that shows by optimizing the profile during the wafer firing process, a significant gain of .51% is achievable.  .51% is HUGE, which can easily translate into hundreds of thousands of dollars in increased revenues per solar manufacturing line.  That’s even in today’s depressed silicon market.

(Click here to view full article)

The thermal process of the wafer is one of the keys to achieving improved efficiencies. Drying steps are expected to remove most of the solvent used in the pastes before entering the firing zones. Solar cell metallization generally follows a spike profile type. Wafers only see peak temperature for approximately 1-4 seconds based on wafer and metallization chemistries. The most important steps include the clean burnout of the organics in the paste followed by etching through the silicon nitride (or other) passivation/ARC layer and, ultimately, the formation of good ohmic contact between the sintered silver and the very top layer of n-type silicon. These all lead to low contribution from series resistance and recombination resulting from the formation of the contacts. Control of this profile will become more crucial as the emitter depth decreases with increasing sheet resistance. Both uniformity of diffusion and furnace will be necessary to achieve the desired efficiency improvements.

The article walks you step by step through the study, here is an extend excerpt from the article related to profiling:

The base line profile on these wafers had been developed prior to the project based on extensive knowledge of the paste chemistry and years of practical experience with the metallization process. The base line profile can be seen in dark blue in Figure 1. For the base line test, as with all the subsequent process improvement tests, the wafers were processed at the same time and fired under the same conditions. Ten wafers were run through the furnace within a short period of time, and all were subjected to the same profile. After firing, we measured the cell efficiency in our continuous lamp tester. The average efficiency for the base line profile was 15.53 percent, as can be seen in Figure 2 (η Cell). Based on the type of wafer that was selected for this study, and the fact that a continuous lamp tester was used rather than a flash tester, this efficiency number was considered good. Now we wanted to make it better.


Figure 1: The wafer profiles for each group

It is important to acknowledge that what we were trying to accomplish was not to find a single “golden” profile for the wafers, but rather the optimal thermal process window. The Heraeus paste SOL9235H is a very robust paste that can perform well throughout a range of profiles. Establishing a thermal process window will set the upper and lower limits for the wafer’s peak temperature, time above certain temperature levels, etc. within which the cell efficiencies will be highest.

Figure 2: Cell efficieny testing

Figure 2: Cell efficieny testing

Figure 3: Boxplot of cell efficiencies for base wafer profile

Figure 3: Boxplot of cell efficiencies for base wafer profile

Since we did not yet know the upper and lower limits to our process window, we used the base line profile as a starting point, and we initially set relatively wide process limits around it as shown in Figure 4. The profiler software always measures how well the profile fits the chosen process window with a single number called Process Window Index (PWI). The PWI number is 100 percent when the profile is at the edge of the process window. The lower the number, the closer the profile is to the center of the process window. A PWI of 0 percent represents a profile at the very center of the process window.

Figure 4: Original Process Window

Figure 4: Original Process Window

Our KIC profiler also has profile simulation software that allowed us to change the furnace zone temperatures or conveyor speed in the software, and to immediately predict the resulting wafer profile. For the first process improvement step, we suspected that a higher peak temperature would benefit the metallization. We tried a few zone temperature changes in the software and studied the software simulation of the corresponding profile before settling on a 10°C increase in the furnace peak zones (Zone 5 and 6). Once the furnace stabilized on the new settings, we ran a set of 10 wafers for our Group 2 test. The average cell efficiency increased from 0.40 to 15.93 percent. For Group 3, we increased the peak temperatures settings in zones 5 and 6 another 10°C, but the average cell efficiency of the 10 wafers dropped by 0.12 percent.

For the Group 4 test, we set the zones back to the Group 2 level and reduced the furnace conveyor speed. The prediction software showed the impact on the wafer profile both in terms of peak temperature changes and, in particular, in terms of time above the various temperature levels shown in Figure 4. Due to this, we reduced the conveyor speed from 200 to 190″/min. The average cell efficiencies increased yet another 0.11 percent above the Group 2 numbers to a cell efficiency of 16.04 percent. Our final test for Group 5 kept the temperatures stable but increased the conveyor speed from 190 to 210″/min. That dropped the average cell efficiency by 0.16 percent.

Figure 5: e-Clispe TC attachment fixture

Figure 5: KIC's e-Clispe TC attachment fixture


By systematically changing certain key profile dimensions, such as peak temperature and time above 500°C, we were able to identify the “sweet spot” in the metallization process. The PWI index and the profiler’s simulation software allowed us to quickly identify the appropriate furnace settings for profiles below, above and in the middle of the optimal settings. This sweet spot yielded an average cell efficiency of 0.51 percent higher than previous experiments had allowed.

The Heraeus SOL 9235H silver paste’s properties allow for high-efficiency processing in a range of profiles, hence a process window can be established around the “ideal” profile identified above. Heraeus now advices its clients to the appropriate process window for each application.

With modern profilers, solar cell manufacturers can adjust their furnace setup until the wafer profile is positioned within the suggested process window. Over time, the thermal process will drift due to a number of variables such as heating lamps changing as they get older, wear and tear in the furnace, conveyor speed drifts, exhaust changes, and more. It then is a simple task for the manufacturing engineer to run another profile, and to use the profiler process optimization software to identify the furnace settings that will yield the appropriate profile.

This method for process optimization depends on accurate and repeatable profile readings. One excessive noise in the profile readings historically has been caused by the attachment method for the TCs. Both cemented and dummy wafer TCs tend to measure the material used to secure the TCs in place, rather than to measure the surface of the wafer. Pinning the TC to the wafer with a weight suffers from non-repeatability. The fixture with flattened TC beads has worked well for us.

Finally, process optimization must be quick and easy enough to be useful for volume production lines, as opposed to only the laboratory line. There is little use in perfecting the process in the laboratory just to see the transfer to the production lines fail because the furnace properties are different. Once the correct process window is established, the high-volume furnaces can be adjusted within minutes, keeping production downtime to a bare minimum. This task must not only be performed during transfer from the lab to the production line, but it also must be performed periodically due to the drift in the thermal process that is a fact of life in any production line. The few minutes it takes to adjust the production furnaces for peak performance is richly rewarded by the ability to consistently produce higher efficiency cells.

Future Studies

The temperature readings taken by the e-Clipse TC attachment fixture are higher than historic readings taken by older TC attachment methods. A future study will focus on quantifying the accuracy and repeatability of the new profiling method as it relates to the theoretical true wafer surface temperatures.

More information: Bjorn Dahle, president of KIC, +1-619-300-5586.